| 性能项目 | 测试方法 | 试验条件[状态] | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.60 | g/cm3 | |
| 吸水率 | ASTM D570 | 24hr,23℃ | 0.23 | % | |
| 水分含量 | ASTM D570 | 50℃ | 0.65 | % | |
| 机械性能 | 拉伸强度 | ASTM D638 | 23℃ | 56 | MPa |
| 拉伸伸长率 | ASTM D638 | 断裂 | 4.0 | % | |
| 弯曲模量 | ASTM D790 | 23℃ | 3270 | MPa | |
| 弯曲模量 | ASTM D790 | 260℃ | 1860 | MPa | |
| 弯曲强度 | ASTM D790 | 23℃ | 76 | MPa | |
| 弯曲强度 | ASTM D790 | 260℃ | 38 | MPa | |
| Izod缺口冲击强度 | ASTM D256 | 23℃ | 21.3 | J/m | |
| Izod无缺口冲击强度 | ASTM D4812 | 23℃ | 112 | J/m | |
| 洛氏硬度 | ASTM D785 | 40-55 | |||
| 电气性能 | 表面电阻率 | ASTM D257 | 4.0E+12 | ohms | |
| 体积电阻率 | ASTM D257 | 4.0E+12 | ohm.cm | ||
| 介电强度 | ASTM D149 | 23℃,2.0mm | 23 | kV/mm | |
| 介电常数 | ASTM D150 | 23℃,100Hz | 5.08 | ||
| 介电常数 | ASTM D150 | 23℃,10kHz | 5.02 | ||
| 介电常数 | ASTM D150 | 23℃,1MHz | 4.72 | ||
| 耗散因数 | ASTM D150 | 23℃,100Hz | 0.0025 | ||
| 耗散因数 | ASTM D150 | 23℃,10kHz | 0.01 | ||
| 耗散因数 | ASTM D150 | 23℃,1MHz | 0.026 | ||